An in vitro evaluation of antimicrobial activity of a fast

Apr 07, 2023

Scientific Reports volume 12, Article number: 16021 (2022) Cite this article

837 Accesses

Metrics details

The aim of this study is to evaluate the antimicrobial activity of the fast-setting iRoot Fast Set Root Repair Material (iRoot FS), Mineral trioxide aggregate (MTA) and Biodentine. The materials were freshly mixed or set for 1 and 7 days to conduct the agar diffusion test, direct contact test and carry-over effect test against E. faecalis and P. gingivalis, and the pH values were also measured. The data were analyzed by an analysis of variance and one-way ANOVA or Dunnett's T3 test, and the Tukey's post hoc test for multiple comparisons (α = 0.05). In the direct contact test, all three materials showed good antibacterial activity after setting for 20 min. The antibacterial properties of the three materials decreased with the increase of setting time (p < 0.05). The suspension of all the three materials showed high pH values (11–12) and no significant difference was observed (p > 0.05). With the extension of setting time, the pH of iRoot FS and Biodentine slightly decreased (p < 0.05). Fresh iRoot FS, Biodentine, and MTA killed E. faecalis and P. gingivalis effectively, but their antimicrobial effect decreased after 24 h, and distinctly decreased after 7 days after mixing. iRoot FS, Biodentine, and MTA showed a tendency of alkalinity during this 7-day experiment.

Endodontic surgery is an option to preserve teeth suffering from non-healing apical periodontitis when root canal retreatment has failed or is not possible1. An ideal root-end filling materials should possess certain characteristics, including biocompatibility, sealing ability, dimensional stability and low solubility2. Also, an ideal root-end filling material should possess antimicrobial activity to inhibit bacteria growth to prevent endodontic surgical failure caused by further microleakage3.

Mineral trioxide aggregate (MTA) is known as the "gold standard" for root-end filling material for its strong clinical performance4. In recent years, several kinds of materials went to the open-market2. Biodentine is a new version of calcium-silicate based inorganic cement and is commercially claimed to be a ‘bioactive dentine substitute’5. Further, a novel premixed calcium phosphate silicate cement, iRoot Fast Set Root Repair Material (iRoot FS, Innovative Bioceramix) was introduced to the market recently and has been used as a permanent root canal repair material in endodontic treatments and apical surgery6.

Previous study results were inconsistent in terms of measuring the antimicrobial activity of the retrograde filling materials used. MTA products were investigated in many articles through inconsistent methods7,8,9, There were also a few studies conducted on Biodentine10,11 , and none was found for iRoot FS. Therefore, the aim of this study was to evaluate the antimicrobial activity of these three retrograde filling materials: MTA, Biodentine, and iRoot FS.

Five microgram of the ProRoot MTA (Dentsply, York County, PA, USA), Biodentine™ (Septodont, Saint Maur des Fosses, France) and iRoot FS (Innovative Bioceramix, BC, Canada) were prepared according to the manufacturers’ instructions and placed on 5 mm diameter sterile filter papers. The test samples were divided into three groups as described by Damlar et al.3. Briefly, samples tested at 20 min after mixing were designated as ‘fresh samples’, those tested on the first day after mixing were designated as ‘1-day samples’, and those tested on the seventh day after mixing were designated ‘7-day samples’. All the materials were allowed to set in a 100% moist atmosphere at 37 °C before experimenting. For the control groups, 5 mm diameter sterile filter papers were immersed in 0.12% chlorhexidine (CHX) and sterile saline respectively for 5 s before each test.

Oral microorganism strains, E. faecalis (ATCC 19433) and P. gingivalis (ATCC 33277) were obtained from State Key Laboratory of Oral Diseases, Sichuan University, Chengdu, China. E. faecalis were cultivated in brain heart infusion broth (BHI broth, Becton, Dickinson and Company, US) and BHI agar plate, while P. gingivalis were cultivated in BHI broth and blood agar plate supplemented with 0.0005% hemin, 0.0001% vitamin K. Both strains were incubated anaerobically (N2 80%; H2 10%; CO2 10%) at 37 °C.

Bacterial suspension was prepared for each bacterial strain and the turbidity was adjusted to 0.1 OD, which corresponds to approximately 108 colony-forming units (CFU)/mL. Then 100 μL of P. gingivalis suspension was streaked on blood agar plates, while E. faecalis was streaked on BHI agar plates. A sterile scratcher was used to inoculate the bacterial suspension onto the agar plate to achieve a lawn of growth. The plates were dried for 5 s in room temperature before the filter papers coated with the materials, sterile saline or CHX were placed on each plate. The plates were cultured anaerobically (N2 80%; H2 10%; CO2 10%) at 37 °C for 48 h before the diameter of the halo formed around the materials (inhibition zone) was observed. The tests were conducted in triplicate.

The filter papers coated with the materials or sterile saline were placed at the bottom of 96-well plates, followed by 200 μL of the bacteria suspension (107 CFU/mL) being added in each well in direct contact with the materials. After being cultured at 37 °C anaerobically for 1 h, the bacteria suspension transferred from each well were serially diluted. The survival of the microorganisms was determined by culturing 100 µL aliquots on BHI agar plates after they were serially diluted 103–105 fold. Then the colonies on the plates were counted and the CFU/mL value was calculated. The loss of viability was calculated by the following formula: loss of viability = (CFU control–CFU sample)/CFU control. The tests were conducted in triplicate.

The carry-over effects of the retrograde filling materials were assessed with procedures described by Ozcan et al.12 with some modifications. The filter papers coated with the materials or sterile saline were placed at the bottom of 96-well plates, and sterile saline (20 μL) was placed in direct contact with the materials. After incubation at 37 °C for 1 h, 230 μL of culture broth was added to each well. After mixing gently with a pipette, 20 μL of the broth was transferred to a tube containing 960 μL of culture broth. Then 20 μL of the bacteria suspension (1.5 × 108 CFU/ml) was added to the tube. Ten-fold serial dilutions were prepared and plated onto BHI agar plates for colony forming. After incubation at 37 °C for 48 h, survival of the bacteria was compared between experimental groups and control group to investigate the antimicrobial activity of the materials. The tests were conducted in triplicate.

For the pH value measurement, 25 mg of each endodontic material were mixed and evenly spread on the bottom of the 24-well plate and were allowed to set in a 100% moist atmosphere at 37 °C before experimenting, then 1 ml of distilled water (pH = 7.4) were added to each well after 20 min, 1 day and 7 days, respectively. After 1 h, the solution was drawn from the wells and centrifuged at 10,000 rpm for 10 min, and the pH measurement was performed with a Five Easy PluspHFEP20 pH meter (METTLER TOLEDO, Zurich, Switzerland).

The data was subjected to a homogeneity test of variance using Levene's test. Data with homogeneous variance were then statistically compared using one-way ANOVA, with the post hoc Tukey's test. For data that showed heterogeneous variance, Dunnett's T3 test was applied. Statistical analysis was performed using SPSS 21.0 (SPSS Inc., Chicago, IL, USA), and p < 0.05 was considered statistically significant.

No inhibition zone was observed in the agar diffusion test except for the positive control.

The results of the DCT with E. faecalis and P. gingivalis are shown in Fig. 1a and b. The negative controls exhibited bacteria growth in all test periods. All three materials presented highest antimicrobial effect against E. faecalis and P. gingivalis when freshly mixed (p < 0.05). Fresh ProRootMTA, iRoot FS and Biodentine inhibited most E. faecalis (ProRootMTA 77.5%, iRoot FS 91.2%, Biodentine 80.7%), However, the antimicrobial activity of iRoot FS against E. faecalis were lower than the other two materials after setting for 1 or 7 days (p < 0.05). As for the antimicrobial activity against P. gingivalis, Fresh ProRootMTA and Biodentine inhibited almost all P. gingivalis (ProRootMTA 97.9%, Biodentine 98.9%) while iRoot FS inhibited the growth of all P. gingivalis (100%). However, no statistical significance was observed between the materials. iRoot FS and Biodentine produced almost complete inhibition after setting for 1 day, while the effect of MTA was relatively lower (p < 0.05). The 7-day samples of the three test materials showed significantly lower growth inhibition of P. gingivalis when compared with the other time interval groups (p < 0.05), while Biodentine showed relatively highest antimicrobial effect (p < 0.05).

Outcome of direct contact test against (a) E. faecalis and (b) P. gingivalis.

Carry-over of the antimicrobial effect from the materials was not observed (P > 0.05) (Fig. 2).

Outcome of carry-over effect test against (a) E. faecalis and (b) P. gingivalis.

pH values of the leachate of the materials are shown in Table 1. All three endodontic materials showed significantly strong alkaline effect in all observed time intervals. No significant difference was noticed when freshly mixed among the materials, and iRoot FS presented lowest pH values after setting for 1 or 7 days (P < 0.05).

The DCT used in the present study is a quantitative and reproducible method to simulate the contact of the microorganism with retrograde filling materials13. This procedure allows us to assess the antimicrobial effect of test materials at different stages of the setting reaction, and also helps to determine whether the data reflect bactericidal, or just bacteriostatic effects, regardless of the diffusion rates of the active agents14. In 2009, Zhang et al. reported a modified DCT15, in which the suspension of MTA was obtained to contact the bacteria suspension. However, since the retrograde filling materials were in direct contact with the microorganisms inside the resected root canals16, the DCT applied in the present study might better mimic the clinical situation. The agar diffusion test (ADT) is another method to evaluate the antimicrobial activity of root-end filling materials3. Since the outcome of ADT depend on the material diffusibility in the medium3 , the solid root-end filling materials may not be diffusible, which could be a possible explanation for the negative outcome of ADT in the present study. Therefore, DCT seems more appropriate in evaluating the antimicrobial activity of solidified materials.

The results of DCT might be affected by carry-over effect of the materials since it can cause the growth inhibition of tested micro-organisms17,18. In the present study, no carry-over effect was observed. Since the root-end filling materials are insoluble, this result is expected. Therefore, the following discussion and conclusion are based on the results of DCT.

MTA was introduced innovatively as a root-filling material by Dr. Torabinejad in 199519. According to previous studies20,21, the antibacterial and antifungal properties of MTA were associated with elevated pH value. In the present study, direct contact test revealed antimicrobial effect of MTA against both E. faecalis and P. gingivalis. A previous study2 by Parirokh et al. showed that MTA exerts antibacterial effects against some facultative bacteria but not on any species of absolute anaerobes, however, another study by Kim et al.22 found that freshly mixed ProRoot MTA formed a bacterial growth inhibition zone against P. gingivalis in disk diffusion test. Since MTA has been tested in many researches but with contradictory results20 such difference may be attributed to the usage of different methodologies, bacterial strains, aerobic and anaerobic conditions.

Biodentine was developed as dentin replacement material. In addition to shorter setting time, it was also reported to be less porosity and less leakage23, less tooth discolors24,25,26 and excellent biocompatibility27 compared with MTA. In the present study, the antimicrobial effect of Biodentine against E. faecalis was similar to that of MTA, and the effect was lower when tested 7 days after setting, which is in accordance with a previous study by Koruyucu et al.13. Since the materials were kept in 100% humidity at 37 °C during the curing phase, one explanation could be that the antimicrobial components were continuously released along with the decrease of pH3.

iRoot FS (Innovative Bioceramix, Vancouver, BC, Canada) was introduced as a root canal repair material. As a premixed material, iRoot FS solidifies only when exposed to a moist environment. Previous studies have reported that iRoot FS has similar apical sealing ability and mechanical properties to MTA28 and that iRoot FS has a shorter setting time (initial 18 min and final 57 min) than MTA. There are great potentials for the clinical application of iRoot FS as the material is cytocompatible while facilitating cell adhesion, proliferation, differentiation and maintenance of normal cell function29. However, the antimicrobial effect of iRoot FS is unknown. In the present study, iRoot FS showed satisfactory antimicrobial effect when tested 20 min or 1 day after setting, and the effect became relatively lower than MTA and Biodentine when tested 7 days after setting, which might be attributed to its shorter setting time.

The pH values measured in this study were between 11 and 12, all the three materials showed strong alkaline pH, which is in accordance with previous studies20,30. However, though Biodentine exhibited the highest pH value at all time intervals, which might explain its superior antimicrobial effect 7 days after setting, it did not show the strongest antibacterial activity against E. faecalis. Therefore, as Zhang et al. mentioned in a previous study31, the antibacterial action cannot be rationally explained by pH alone. Moreover, in clinical situations, a desirable high pH after MTA application cannot be maintained due to the buffering capacity of dentin22.

The use of a single-species planktonic bacteria model is an evident limitation of our study. According to a previous study, the microbiota of persistent periapical infection is polymicrobial with predominance of E. faecalis and P. gingivalis, regardless of the method used for microbial identification32. Hence, E. faecalis and P. gingivalis were used in this study to appraise the antimicrobial property of these materials. However, in an infected root canal, a large number of microorganisms occur in parallel in the form of multispecies biofilms. Though simplified laboratory models do not represent the clinical reality of the infected root canal, they constitute valuable tools to preliminarily assess the antibacterial effect of endodontic materials, as they can be standardized and controlled16. This study provided a main insight into the antimicrobial effect of iRoot FS, and further studies against biofilms33 or in vivo studies are required to better understand the various properties of the retrograde filling materials.

According to the findings of this study, fresh iRoot FS, Biodentine, and MTA killed E. faecalis and P. gingivalis effectively, but their antimicrobial effect decreased after 24 h, and distinctly decreased after 7 days after mixing. iRoot FS, Biodentine, and MTA showed a tendency of alkalinity during this 7-day experiment.

The datasets generated during and/or analyzed during the current study are available from the corresponding author on reasonable request. All data generated or analyzed during this study are included in this published article.

Kohli, M. R., Berenji, H., Setzer, F. C., Lee, S. M. & Karabucak, B. Outcome of endodontic surgery: A meta-analysis of the literature-part 3: Comparison of endodontic microsurgical techniques with 2 different root-end filling materials. J. Endod. 44, 923–931 (2018).

Article Google Scholar

Parirokh, M. & Torabinejad, M. Mineral trioxide aggregate: A comprehensive literature review–part I: Chemical, physical, and antibacterial properties. J. Endod. 36, 16–27 (2010).

Article Google Scholar

Damlar, I., Ozcan, E., Yula, E., Yalcin, M. & Celik, S. Antimicrobial effects of several calcium silicate-based root-end filling materials. Dent. Mater. J. 33, 453–457 (2014).

Article CAS Google Scholar

Kollmuss, M., Preis, C. E., Kist, S., Hickel, R. & Huth, K. C. Differences in physical characteristics and sealing ability of three tricalcium silicate-based cements used as root-end-filling materials. Am. J. Dent. 30, 185–189 (2017).

PubMed Google Scholar

Malkondu, Ö., Karapinar, K. M. & Kazazoğlu, E. A review on biodentine, a contemporary dentine replacement and repair material. Biomed. Res. Int. 2014, 160951 (2014).

Article Google Scholar

Liu, Y. et al. Cell migration and Osteo/Odontogenesis stimulation of iRoot FS as a potential apical barrier material in apexification. Int. Endod. J. 53, 467–477 (2020).

Article CAS Google Scholar

Morita, M. et al. Antibacterial activities and mineral induction abilities of proprietary MTA cements. Dent. Mater. J. 40, 297–303 (2021).

Article CAS Google Scholar

Khedmat, S., Aminipor, M., Pourhajibagher, M., Kharazifar, M. J. & Bahador, A. Comparison of antibacterial activities of ProRoot MTA, OrthoMTA, and RetroMTA against three anaerobic endodontic bacteria. J. Dent (Tehran). 15, 294–299 (2018).

PubMed Central Google Scholar

Queiroz, M. B. et al. Physicochemical, biological, and antibacterial evaluation of tricalcium silicate-based reparative cements with different radiopacifiers. Dent. Mater. 37, 311–320 (2021).

Article CAS Google Scholar

Nikhil, V., Madan, M., Agarwal, C. & Suri, N. Effect of addition of 2% chlorhexidine or 10% doxycycline on antimicrobial activity of biodentine. J. Conserv. Dent. 17, 271–275 (2014).

Article Google Scholar

Deveci, C., Tuzuner, T., Cinar, C., Odabas, M. E. & Buruk, C. K. Short-term antibacterial activity and compressive strength of biodentine containing chlorhexidine/cetirimide mixtures. Niger. J. Clin. Pract. 22, 227–231 (2019).

CAS PubMed Google Scholar

Ozcan, E., Yula, E., Arslanoğlu, Z. & Inci, M. Antifungal activity of several root canal sealers against Candida Albicans. Acta Odontol. Scand. 71, 1481–1485 (2013).

Article Google Scholar

Koruyucu, M. et al. An assessment of antibacterial activity of three pulp capping materials on enterococcus faecalis by a direct contact test: An in vitro study. Eur. J. Dent. 9, 240–245 (2015).

Article Google Scholar

Eldeniz, A. U., Hadimli, H. H., Ataoglu, H. & Orstavik, D. Antibacterial effect of selected root-end filling materials. J. Endod. 32, 345–349 (2006).

Article Google Scholar

Zhang, H., Pappen, F. G. & Haapasalo, M. Dentin enhances the antibacterial effect of mineral trioxide aggregate and bioaggregate. J. Endod. 35, 221–224 (2009).

Article Google Scholar

Kapralos, V. et al. The dentine-sealer interface: Modulation of antimicrobial effects by irrigation. Int. Endod. J. 55, 544–560 (2022).

Article Google Scholar

Huang, Y. et al. The in vitro antimicrobial activities of four endodontic sealers. BMC Oral Health 19, 118 (2019).

Article Google Scholar

Zhang, H., Pappen, F. G. & Haapasalo, M. Dentin enhances the antibacterial effect of mineral trioxide aggregate and bioaggregate. J. Endod. 35, 221–224 (2009).

Article Google Scholar

Torabinejad, M., Rastegar, A. F., Kettering, J. D. & Pitt, F. T. Bacterial leakage of mineral trioxide aggregate as a root-end filling material. J. Endod. 21, 109–112 (1995).

Article CAS Google Scholar

ElReash, A. A. et al. Antimicrobial activity and pH measurement of calcium silicate cements versus new bioactive resin composite restorative material. BMC Oral Health 19, 235 (2019).

Article Google Scholar

Bhavana, V. et al. Evaluation of antibacterial and antifungal activity of new calcium-based cement (biodentine) compared to MTA and glass Ionomer Cement. J. Conserv. Dent. 18, 44–46 (2015).

Article Google Scholar

Kim, R. J., Kim, M. O., Lee, K. S., Lee, D. Y. & Shin, J. H. An in vitro evaluation of the antibacterial properties of three mineral trioxide aggregate (MTA) against five oral bacteria. Arch. Oral Biol. 60, 1497–1502 (2015).

Article CAS Google Scholar

Refaei, P., Jahromi, M. Z. & Moughari, A. Comparison of the microleakage of mineral trioxide aggregate, calcium-enriched mixture cement, and biodentine orthograde apical plug. Dent. Res. J. (Isfahan) 17, 66–72 (2020).

Article Google Scholar

Kohli, M. R., Yamaguchi, M., Setzer, F. C. & Karabucak, B. Spectrophotometric analysis of coronal tooth discoloration induced by various bioceramic cements and other endodontic materials. J. Endod. 41, 1862–1866 (2015).

Article Google Scholar

Shokouhinejad, N., Nekoofar, M. H., Pirmoazen, S., Shamshiri, A. R. & Dummer, P. M. Evaluation and comparison of occurrence of tooth discoloration after the application of various calcium silicate-based cements: An ex vivo study. J. Endod. 42, 140–144 (2016).

Article Google Scholar

Marconyak, L. J. et al. A comparison of coronal tooth discoloration elicited by various endodontic reparative materials. J. Endod. 42, 470–473 (2016).

Article Google Scholar

Ghilotti, J. et al. Comparative surface morphology, chemical composition, and cytocompatibility of Bio-C repair, Biodentine, and ProRoot MTA on hDPCs. Materials (Basel) 13, 2189 (2020).

Article ADS CAS Google Scholar

Shi, S., Zhang, D. D., Chen, X., Bao, Z. F. & Guo, Y. J. Apical sealing ability of bioceramic paste and mineral trioxide aggregate retrofillings: A dye leakage study. Iran Endod. J. 10, 99–103 (2015).

CAS PubMed PubMed Central Google Scholar

Luo, T., Liu, J., Sun, Y., Shen, Y. & Zou, L. Cytocompatibility of biodentine and iRoot FS with human periodontal ligament cells: An in Vitro study. Int. Endod. J. 51, 779–788 (2018).

Article CAS Google Scholar

Quintana, R. M. et al. Bone tissue reaction, setting time, solubility, and pH of root repair materials. Clin. Oral Investig. 23, 1359–1366 (2019).

Article Google Scholar

Zhang, H., Shen, Y., Ruse, N. D. & Haapasalo, M. Antibacterial activity of endodontic sealers by modified direct contact test against enterococcus faecalis. J. Endod. 35, 1051–1055 (2009).

Article Google Scholar

Barbosa-Ribeiro, M. et al. Microbiological analysis of endodontically treated teeth with apical periodontitis before and after endodontic retreatment. Clin. Oral Investig. 25, 2017–2027 (2021).

Article Google Scholar

Ruiz-Linares, M., de Oliveira, F. J., Solana, C., Baca, P. & Ferrer-Luque, C. M. Current status on antimicrobial activity of a tricalcium silicate cement. J. Oral Sci. 64, 113–117 (2022).

Article CAS Google Scholar

Download references

These authors contributed equally: Mengzhen Ji and Yaqi Chi.

State Key Laboratory of Oral Diseases, Sichuan University, National Clinical Research Center for Oral Diseases, Department of Endodontics, West China Hospital of Stomatology, Sichuan University, Chengdu, 610041, China

Mengzhen Ji, Yaqi Chi, Ye Wang, Kaixin Xiong, Xuan Chen & Ling Zou

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

M.J. and L. Z. designed the study. Y. C., M. J., Y. W.and K. X. conducted the study and prepared the figures and the table. M. J., Y. C. and Y. W. analyzed the data. M. J., Y. C. and X. C. drafted the manuscript. X. C. and L. Z. revised the manuscript critically for important intellectual content.

Correspondence to Ling Zou.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

Ji, M., Chi, Y., Wang, Y. et al. An in vitro evaluation of antimicrobial activity of a fast-setting endodontic material. Sci Rep 12, 16021 (2022). https://doi.org/10.1038/s41598-022-20454-7

Download citation

Received: 12 May 2022

Accepted: 13 September 2022

Published: 26 September 2022

DOI: https://doi.org/10.1038/s41598-022-20454-7

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.